Pressure-Sensitive Adhesives 101

October 1, 2009


Pressure-sensitive adhesives (PSAs) are used in applications ranging from labeling food packaging to assembling electronic devices to mounting graphics displays. Although they have been around for decades and their use is widespread, manufacturers, converters, and printers may not understand the key differences between the adhesive choices available, how they’re constructed, or which are best suited for a particular job.

This article explains what a PSA is, how it’s constructed and what adhesive options are available. The advantages and disadvantages of the primary adhesive types will be addressed, as well as how they are formulated and their common applications.

What is a PSA?

A pressure-sensitive adhesive is a material that holds two surfaces together solely by surface contact, which is achieved by slight initial external pressure. These dry adhesives require no activation with water, solvent or heat, and firmly adhere to many dissimilar surfaces with minimal pressure. Aggressive and permanently tacky at room temperature, PSAs can be used for bonding materials such as plastic, paper, metal, glass, and wood.

Pressure-sensitive adhesives offer numerous advantages. Application can be easily automated and usually requires no elaborate equipment. When used in assembly, PSAs save time compared to liquid adhesives because they don’t require any setup or long curing times. In addition, adhesion is immediate, allowing manufacturing procedures to continue uninterrupted, which results in significant time and labor savings. Pressure-sensitive adhesives eliminate the need for screws, rivets, clips or drilling holes, thus preventing cracks and corrosion and improving the integrity and appearance of the final product. PSAs also provide an insulating seal, as well as sound and vibration control.

PSA Constructions



Manufacturing Methods for PSAs

There are four popular chemistries resulting in a pressure-sensitive adhesive laminate. One chemistry is achieved through the use of a solvent. With this method, the adhesive components (usually rubber or acrylic) are dissolved in a solvent and then coated onto a web. The solvent is then evaporated using heat and air flow, leaving a dry yet sticky adhesive (pressure-sensitive) that is wound in a roll.

Adhesives made with solvents often provide high performance, but can be expensive and require extra care because of processing restrictions. Special equipment is needed to properly dispose of the solvent, and there must be vigilant awareness of safety issues when dealing with solvents.

Another way to manufacture a PSA is to create an emulsion (water-based). Here, the acrylic polymer and other additives are dispersed, not dissolved, in water and coated onto a web. Again, heat and air flow are used to evaporate the water before winding into a roll. Today’s water-based emulsions can often provide the same high level of performance as solvent-based acrylics and are generally a good choice when lower cost and safety are important, since water-based emulsions don’t require the extra steps that are needed with solvents.

The third method for creating a pressure-sensitive adhesive is developing a hot-melt. Hot melts are typically a mixture of a polymer (such as thermoplastic rubber), tackifying resins and a hydrocarbon diluent (wax or oil plasticizer), which is heated until flowable. The hot-melt adhesive is then coated on a web and cooled before winding into a roll.

Hot-melt adhesives typically exhibit excellent adhesion to substrates and facestocks, have very good coatability, and are less expensive than most solvent-based adhesives. Drawbacks generally include processing and safety challenges, as well as difficulty performing under high temperatures. The major advantage of a hot-melt system is its lack of solvents and water - meaning it doesn't have to be dried in an oven. Hot melts are frequently referred to as 100%-solids (no water or solvent) technology.

Finally, PSAs can be created through the use of a UV-curable adhesive. These adhesives usually require no mixing and cure in seconds when exposed to a UV light source. These environmentally friendly adhesives are reactive compounds that contain no solvents or other volatile substances. Because UV adhesives cure so quickly and at temperatures much lower than thermal heating, they can be used successfully on several heat-sensitive substrates such as plastic films, paper, and synthetic fibers. The quick curing minimizes shrinkage, providing the dimensional accuracy that is often called for in applications such as electronics manufacturing. UV-curable adhesives also offer durability, strength, insulation characteristics, and resistance to chemicals, moisture, and temperature. Like hot melts, UV adhesives do not require an oven.

A decision on which method of adhesive manufacturing technology should be used for a particular application is determined by the performance characteristics needed.

Chart.

Common Adhesive Types and Their Properties

In addition to considering the method in which the adhesive is created (solvent-based, water-based, hot melt, or UV-cured), it is important to understand the key adhesive component choices and how they will affect the PSA’s performance in the application. The three main adhesive chemistry options are rubber/resin, acrylic and silicone.

For many years, rubber/resin formulations have been available that combine natural or synthetic rubber with tackifying resins, oils, antioxidants, or other ingredients as needed. They are typically either solvent-based or used in hot melts, and the aggressive nature of rubber adhesives makes excellent bonding easy to achieve.

These adhesives are known for their high level of adhesion to a variety of substrates and facestocks, as well as their high coatability. Rubber-based adhesives provide high tack and peel, and make excellent general-purpose adhesives, because of their ability to adhere well to several non-polar, low-energy surfaces, including polyethylene and polypropylene. In general, rubber-based adhesives are often a more economical choice compared to most acrylics.

Disadvantages of rubber-based adhesives include limited effectiveness when exposed to certain chemicals, UV rays, or high temperatures (over 150°F/66°C). In addition, they are more susceptible to oxidation and may darken, lose their tack, and become brittle if overexposed. Also, rubber/resin adhesives may turn soft and gummy if plasticizers, used in most polyvinyl chloride films (PVC), migrate into the adhesive.

The other type of adhesive chemistry commonly used in PSAs is acrylic. Acrylic adhesives can either be solvent- or water-based, and are formulated by reacting monomers with the desired properties, which are then typically crosslinked to form the type of polymer needed. Monomers are the building blocks of polymers and are considered to be either “soft” or “hard.” The combination of hard and soft monomers can be adjusted based on the level of adhesive (polymer) performance needed.

Crosslinking polymers improves the cohesive strength (internal strength of the adhesive, or the ability to stick to itself) of the acrylic formulation and can be accomplished in one of three ways: the use of thermal heat energy; by self-curing when a solvent is removed during the drying process; or through UV or EB non-thermal radiation.

In general, acrylics are relatively firm and durable, but are not as aggressive as rubber-based adhesives. An acrylic adhesive can be modified to alter its adhesion properties based on the selection of monomers used, the level of polymerization created, or by adding tackifying resins or other chemicals.

The advantages of acrylic adhesives are typically the opposite of rubber adhesives. Acrylics provide excellent temperature, UV and oxidation resistance; therefore, they are often the preferred choice for outdoor applications. They resist the negative plasticizing action that can occur with rubber and hold up well to chemical exposure. Acrylic-based adhesives are very durable and have clarity and color stability. Acrylics bond well to polar surfaces like metal, glass, polyesters and polycarbonates, and have high peel, tack, and shear.

Disadvantages of acrylics usually include poor adhesion to low-energy surfaces, such as polyethylene and polypropylene, as well as lower overall adhesion compared to rubber unless the adhesive is highly engineered. In general, acrylics are often more expensive than rubber-based adhesives.

Silicone adhesives are another chemical option for PSAs but are less common than rubber or acrylic. These specialized adhesives consist of silicone polymers that provide adhesion to silicon and other hard-to-adhere-to materials. Silicone-based adhesives can maintain adhesion over a range of temperatures; however, beyond their ability to adhere to difficult surfaces, their overall adhesive strength is low. Silicone adhesives are also more expensive.

Final Considerations