While standard light-curing materials cure effectively using UV/Visible light, they often struggle in areas where the light cannot reach, leaving behind uncured areas. These shadowed regions not only compromise the reliability of the final product but can also weaken adhesive bonds over time. Dymax reports that HLC addresses the issue of incomplete curing in dark areas with rapid moisture/contact cure capability. Bonding to a broad range of substrates, including opaque and light-blocking materials, is also possible.

Due to the composition of their light-curing component, Dymax HLC adhesives form a cross-linked polymer framework, enabling the successful bonding of small gaps or larger joints. Light-curing also reduces the risk of "blooming," a common issue with cyanoacrylates, where a white residue forms at the edges of bond lines when they react with ambient humidity. Light-curing can significantly reduce the risk of blooming as the material cross-links before the monomer can volatilize.

The first adhesive in the series, Dymax HLC-M-1000 is engineered for medical applications and meets several biocompatibility standards. Its light-curing capabilities allow for rapid curing in seconds with low-intensity light, optimizing performance even at ~20 mW/cm². With an extremely low viscosity of 3 cP, the material is capable of wicking into extremely tight bond joints not typically accessible with other, higher-viscosity adhesives.

Learn more at https://dymax.com.